Phosphinate flamma retardant pro Polyester Iniectio CUMATIUM Applications

PHOSPHINATUS FLAMMA RETARDANTIS POLYESTER INiectio APPLICATIONIS-ALUMINII HYPOPHOSPHITE (Al (H2 PO2)3, phosphorus inorganicum flammae retardat quae in specie polyester iniectio fingitur, cum phosphoro contento ≥ 30% et compositione thermarum temperaturam ≥ 280 ℃ habet. summus temperatus processus, et minimam ictum in infusione fingendi processum. Efficit flammam efficientem retardationem in materiis polyester ut PET et PBT per mechanismum gas-phase flammae dualis retardatio et condensatio periodi carbonizationis, servato productum diaphaneitatis et roboris mechanicae. Occurrit signa ut UL94 et GB/T 2408 producitur ad retardatam retardatam, et ad retardationem et condensationem periodi carbonizationis, servato producto diaphano et mechanica vi. PHOSPHINATUS FLAMMA RETARDANT AD POLYESTER INIECTIONEM CUMATIAE APPLICATIONES: Aluminium Hypophosphite (Sulfate Low Content, aht-220B) et regularis Aluminium Hypophosphite (HT-220A) duo generis Aluminium Hypophosphite (Al (H2 PO2)3.

Product Introductio:

1. Tres core commoda accommodandi ad polyester iniectio corona

(1) Temperatio stabilitatis, compatibilis cum iniectione processus coronae

Temperatus resistentiae processus: Compositio temperatura initialis ≥ 280 , altior quam vulgaris temperatura pro infusione coronae polyester (PET: 240-280 ; PBT: 220-260 ), ad vitandam praematura compositionem et productionem bullae vel degradationis productorum in processu, ut superficies lenitas producti (gloss. ≥ 85GU);

Diu terminus calor resistentia: Post iniectio fingens, productum diu ad 150 adhiberi potest, cum flamma retardatio effectus retentionis rate of ≥ 95%, apta ad polyester components quae requirit caliditas resistentiae.

(II) High dispersibilitatem efficit productum uniformitatem

Magnitudo particula nanoscales: D50=2-5 µ m, superficies cum acido stearico modificata, in liquefactione polyester uniformiter dispersa sine agglomeratione, vitans "plaga zebra" vel inaequales proprietates mechanicas in injectione partium formatarum;

Viscositas humilis effectus: 10-15% aluminii hypophosphitae addens ad polyester liquefactum reducit indicem liquefactum (MFR) per 12% ≤ (melius quam 25% reductionem flammae traditae retardat aluminium hydroxidum), aptam ad praecisionem iniectionem partium fabricarum complexarum faciens.

(3) Dual statera flammae tarditatis et proprietatibus mechanicis

Flamma efficiens retardat: Addens 12-18% consequi potest UL94 V-0 flammam retardat gradus (1.6mm crassitudinis) polyester, auget index oxygeni (OI) ad plus 32%, et nullas stillas vel solum sui ipsius stillulas in combustione exstinguentes;

Mechanica perficiendi conservatio: Roboris tensilis iniectio productorum formatorum est ≥ 75MPa (circiter 10% minus quam polyester puro), flexio modulus est ≥ 2000MPa, et robur ictum est ≥ 8kJ/m , occurrens requisitis mechanicis elementorum structurarum.

2. Dual flamma retardat mechanism augendae salutis effectus

Gas phase flamma retardat: phosphorus emittit coetus activos (sicut H PO ·) in calidis caliditatibus, capit H · et OH · radicales ab polyester combustione generatos, motus combustionis catenam inhibet, et apicem caloris emissio rate plus quam 40% minuit;

Condensata periodus flamma retardat: efficit continuum et densum stratum carbonisatum, crassitudine auctum per 30% comparatum ad ante additionem, efficaciter claudendi oxygeni et caloris translatio, reducendo combustionem durationis (reducendo totum calorem emissio per 50%).

Physica et Chemical Properties

Clavis Commodum

Princeps TGA: TGA(1%) ≥310℃

Princeps Stabilis Quality: puritas maxime stabilis in 96.0% -97.5%

Area application:

1. Electronic et iniectio electrica partium formatur

PET iungo: adhibitis phialas telephonicas et interfaces matricas computatrales. Post 10-12% aluminium hypophosphitem addens, certificationem UL94 V-0 transiit et occurrit CTI (Leakage Traceability Index) ≥ 600V, cum praestanti observantia arcui resistentiae;

PBT nullam habitationem: aptas ad automotivas dispositos, modulorum imperium industriae, filum test calefactorium repugnans (GWIT ≥ 775 ), longi temporis resistentia ad caliditatem ambientis 125 .

2. Lorem components

DELICIAE machinae cucullo componentes: sicut aer colum habitationi, addita cum 15% aluminii hypophosphite, transiit FMVSS 302 flammae experimentum retardans (combustionis rate ≤ 50mm/min), resistens machinae corrosioni olei (SAE 10W-40 maceratae per 72 horas, retentio rate ≥ 95%).

PBT cinematographicae autocineticae electronicae: adhibitae sunt in autocineto camerae modulorum et insterni sensorum, cum utraque flamma retardatio et resistentia impacta (tantum fultum trabem ictum virium ≥ 15kJ/m ).

3. Domus et dolor bonis

PET vasa flammea retardant pellucida: ut proin pixides prandii, cum luce transmissionis ≥ 80% addita 8-10% aluminii hypophosphitae, in obsequio cum GB 4806.7 (commodius cibi materialis), et flammae retardantis rating GB/T 2408 V-2;

PBT supellex ferramentaria: ut cancellos flammeos retardant conportantes et connexiones vestium, certificatum per GB/T 8624 B1 gradum, cum retentione mechanica perficiendi ≥ 90% post resistentiam tempestatis (UV senescit per 500 horas).

Packaging:Net pondus 25kg/peram, compone peram charta-plasticam et aluminium interiorem ffoyle

Repono et Operam:Serva in siccis, locus temperatus et umor, conditio probandi, calefactio prohibens.